<r><QUOTE author="Ravisteam;99856"><s>[QUOTE=Ravisteam;99856]</s>Hi yes i hve the same ad yours and i do print several but some times singles too..tem go up and down like a yoyo lol...i normally do 12 mins ..pepers frm uk too..i recently put the temp down to 180 c and now it seems the effect is ...

<r><QUOTE author="Ravisteam;99668"><s>[QUOTE=Ravisteam;99668]</s>I have printed 100s and all come up same ...If I keep it less mins in the press ink wont transfer properly ..And the same time my press never stays in the same temperature it is in the range of 205C -to 160C keep changing .I only use ...

<r><QUOTE author="Ravisteam;99652"><s>[QUOTE=Ravisteam;99652]</s>thanks for the reply.if i explain it again ,its like when you leave metal inserts in the heat press for bit longer you get the same effet( kind a burnt but its not much visible)..my 3d covers print great too but this effect cant be get ...

Sorry for not replying sooner, Ravisteam. I was on holiday and then ill.
I am not 100% certain of what you mean, however the end results of my cases are clear and sharp. No residue effect from what I can see.

Hello Lindsey.
I have only been here a couple of days myself and can tell you that it is a resourceful place with friendly, helpful people. Enjoy your stay!

<r>This may well be a daft question, but I've seen some bibs which have a vinyl acetate backing. I would assume this could melt or become damaged during the pressing process. Would I be right or has anyone successfully managed to heat press a baby bib with a vinyl acetate backing? (yes I am a newbie ...

<r><QUOTE author="Ucase Ltd;92444"><s>[QUOTE=Ucase Ltd;92444]</s>Now there's a thought!<br/>
<br/>
<br/>
That sounds like a sensible option - I'll look into it.<br/>
<br/>
Thanks!<e>[/QUOTE]</e></QUOTE>

I also have the issue of having a bad smell, and find it affects my asthma. So much so that I ...

Thank you, Justin, for the welcome. Location updated

I also have this, at +/- 10C. I have also had it, when the temperature is set to 220C, to change up and down, dropping as low as 172C.

<r>Are you referring to a specific 3D Heat Press? I use the ST3042, 3D Vacuum Heat Press (Chinese make). Initially I had no end of bother with it but things are coming together now.<br/>
<br/>
For 3D 'hard' phone cases the settings I've found work are:<br/>
Temperature: 190C<br/>
Time: 9 minutes<br ...